全球鋼材百科網(wǎng)
P295GH簡(jiǎn)介

牌號(hào) P295GH
歐標(biāo)鋼號(hào) 1.0481
對(duì)應(yīng)標(biāo)準(zhǔn) EN 10222-2-2017
壓力用途用鋼制鍛件 第2部分 具有高溫特性的鐵素體和馬氏體鋼
Steel Forgings for Pressure Purposes. Part 2:Ferritic and Martensitic Steels with Specified Elevated Temperature Properties
歸類 碳鋼
P295GH 化學(xué)元素成分含量(%)
成分 C Si Mn P S Cr Ni Cu Mo Ti V Nb 更多
最小值 0.08 - 0.9 - - - - - - - - - Cr+Cu+Mo+Ni≤0.70
最大值 0.2 0.4 1.5 0.03 0.025 0.3 0.3 0.3 0.08 0.03 0.02 0.01
碳當(dāng)量計(jì)算
P295GH 機(jī)械性能
厚度
t
mm		 熱處理或狀態(tài)
抗拉強(qiáng)度
σb
Mpa 		屈服點(diǎn)
σs
Mpa 		斷后伸長(zhǎng)率或延伸率
δ
% 		沖擊吸收能量
KV2
J
t≤60 奧氏體化或固溶退火,890~950℃,空冷 460~580 ≥285 I：≥24，tr/t：≥22 I：≥40，tr/t：≥27
60＜t≤100 奧氏體化或固溶退火,890~950℃,空冷 460~580 ≥260 I：≥23，tr/t：≥21 I：≥40，tr/t：≥27
① I = longitudinal to main forging directions；tr = transverse to main forging directions；t = tangential.
② Maximum room temperature for the impact test is 20 °C. By option, impact testing may be carried out at 0°C, with the condition to fulfil the impact values as stated in this table.
③ Until the yield point criteria are harmonized in the various national codes, determination of ReH may be replaced by determination of Rp0.2. In this case Rp0.2 values are 10 MPa lower for ReH values up to 355 MPa and 15 MPa lower for ReH values greater than 355 MPa.
1 近似對(duì)照表 承壓扁鋼制
國(guó)際標(biāo)準(zhǔn)組織 歐標(biāo)
ISO EN 數(shù)字牌號(hào)
P295GH P295GH 1.0481
2 近似對(duì)照表 碳素結(jié)構(gòu)鋼和工程用鋼
日本 美國(guó) 國(guó)際標(biāo)準(zhǔn)組織 德國(guó) 法國(guó) 歐標(biāo) 俄羅斯 瑞典 英國(guó)
JIS ASTM ISO W-Nr. NF EN/NF EN 數(shù)字牌號(hào) GOST SS BS EN/BS
SG365
SPV315
SPV32 		A516Gr.65
X46 		P11 1.0436 A48AP
A48CP
A48FP 		P295GH 1.0481 14G2
18K 		2102
2103 		224-460B
224Gr.460
224Gr.490
430LT
全球鋼材百科網(wǎng)