全球鋼材百科網(wǎng)
F593 410簡介

牌號 F593 410
美國UNS S41000
對應標準 ASTM F593-2017
不銹鋼螺栓、六角螺釘和螺柱標準規(guī)范
Standard specification for stainless steel bolts, hex cap screws, and studs
歸類 馬氏體不銹鋼
F593 410 化學元素成分含量(%)
成分 C Si Mn P S Cr
最小值 - - - - - 11.5
最大值 0.12 1 1 0.04 0.03 13.5
碳當量計算
F593 410 機械性能
公稱直徑
inch
試樣		 熱處理或狀態(tài)
抗拉強度
σb
ksi 		屈服點
σs
ksi 		斷后伸長率或延伸率
δ
% 		硬度
HBW
1/4 ~ 1-1/2 (全尺寸) H 110~140 ≥90 HR (C20~30)
1/4 ~ 1-1/2 (全尺寸) HT 160~190 ≥120 HR (C34~45)
1/4 ~ 1-1/2 (機加工) H ≥110 ≥90 ≥18
1/4 ~ 1-1/2 (機加工) HT ≥160 ≥120 ≥12
注1： “全尺寸”指的拉力測試試件是使用前的狀態(tài)未經(jīng)改變的完整的緊固件產(chǎn)品。
注2：A——Machined from annealed or solution-annealed stock thus retaining the properties of the original material, or hot-formed and solution-annealed.
AF——Headed and rolled from annealed stock and then reannealed.
AH——Solution annealed and age-hardened after forming.
CW——Headed and rolled from annealed stock thus acquining a degree of cold work; sizes 0.75 in. and larger may be hot worked and solution-annealed.
H——Hardened and tempered at 1050°F (565℃) minimum.
HT——Hardened and tempered at 525°F (274℃) minimum.
SH——Machined from strain hardened stock or cold-worked to develop the specified properties.
1 近似對照表 馬氏體不銹鋼
中國 中國臺灣 日本 韓國 美國 國際標準組織 德國 法國 歐標 俄羅斯 瑞典 英國
GB ISC CNS JIS KS ASTM UNS ISO 數(shù)字牌號 DIN EN/DIN W-Nr. NF EN/NF EN 數(shù)字牌號 GOST SS BS EN/BS
12Cr13
(1Cr13) 		S41010 410 SUS 410 STS 410 410 S41000 X12Cr 13 4006-410-00-I X10Cr 13
X12Cr 13 		1.4006
1.4006 		Z12C 13
Z10C13 		X12Cr 13 1.4006 12Х13
12KH13
15KH13L 		2302 410S21
2 近似對照表 馬氏體型耐熱鋼
中國 中國臺灣 日本 韓國 美國 國際標準組織 德國 法國 歐標 俄羅斯 瑞典 英國
GB ISC CNS JIS KS ASTM UNS ISO DIN EN/DIN W-Nr. NF EN/NF EN 數(shù)字牌號 GOST SS BS EN/BS
12Cr13
(1Cr13) 		S41010 410 SUS 410 STS 410 410 S41000 X12Cr 13 X10Cr 13 1.4006 Z12C 13 X12Cr 13 1.4006 12Х13 2302 410S21