Type 403簡(jiǎn)介

牌號(hào) Type 403
美國(guó)UNS S40300
對(duì)應(yīng)標(biāo)準(zhǔn) ASTM A580/A580M-2018
不銹鋼絲
Stainless Steel Wire
歸類 馬氏體不銹鋼
Type 403 化學(xué)元素成分含量(%)
成分 C Si Mn P S Cr
最小值 - - - - - 11.5
最大值 0.15 0.5 1 0.04 0.03 13
碳當(dāng)量計(jì)算
Type 403 機(jī)械性能
條件 熱處理或狀態(tài)
抗拉強(qiáng)度
σb
Mpa 		屈服點(diǎn)
σs
Mpa 		斷后伸長(zhǎng)率或延伸率
δ
% 		斷面收縮率
ψ
% 		硬度
HBW
A 冷精軋 ≥485 ≥275 ≥16 ≥45
A 退火 ≥485 ≥275 ≥20 ≥45
T 冷精軋 ≥690 ≥550 ≥12 ≥40
H 冷精軋 ≥830 ≥620 ≥12 ≥40
t≤9.5mm 955℃，空冷 HRC
≥35
注1：Condition A —— Annealed as a final heat treatment.
Material in Condition A may be given a final cold drawing for size control or finish, or both, slightly raising tensile strength.
Condition T —— Heat treated to an intermediate temper generally by austenitizing, quenching, and tempering at a relatively low temperature.
Condition H —— Heat treated to a hard temper generally by austenitizing, quenching, and tempering at a relatively low temperature.
1 近似對(duì)照表 馬氏體不銹鋼
中國(guó) 中國(guó)臺(tái)灣 日本 韓國(guó) 美國(guó) 俄羅斯 瑞典 英國(guó)
GB ISC CNS JIS KS ASTM UNS GOST SS BS EN/BS
12Cr12
(1Cr12) 		S40310 403 SUS 403 STS 403 403 S40300 08Х13 2301 403S17
2 近似對(duì)照表 馬氏體不銹鋼
中國(guó) 日本 美國(guó) 德國(guó) 法國(guó) 歐標(biāo) 俄羅斯 瑞典 英國(guó)
GB JIS ASTM UNS DIN EN/DIN NF EN/NF EN 數(shù)字牌號(hào) GOST SS BS EN/BS
0Cr13 SUS410S 410S
Type403 		S41008 X7Cr14 Z6C13
Z8C12 		X6Cr13 1.4000 08KH13 2301 403S17