全球鋼材百科網(wǎng)
F593 630簡介

牌號 F593 630
美國UNS S17400
對應(yīng)標(biāo)準(zhǔn) ASTM F593-2017
不銹鋼螺栓、六角螺釘和螺柱標(biāo)準(zhǔn)規(guī)范
Standard specification for stainless steel bolts, hex cap screws, and studs
歸類 馬氏體不銹鋼
F593 630 化學(xué)元素成分含量(%)
成分 C Si Mn P S Cr Ni Cu 更多
最小值 - - - - - 15 3 3 Cb+Ta：0.15~0.45
最大值 0.07 1 1 0.04 0.03 17.5 5 5
碳當(dāng)量計(jì)算
F593 630 機(jī)械性能
公稱直徑
inch
試樣		 熱處理或狀態(tài)
抗拉強(qiáng)度
σb
ksi 		屈服點(diǎn)
σs
ksi 		斷后伸長率或延伸率
δ
% 		硬度
HBW
1/4 ~ 1-1/2 (全尺寸) AH 135~170 ≥105 HR (C28~38)
1/4 ~ 1-1/2 (機(jī)加工) AH ≥135 ≥105 ≥16
注1： “全尺寸”指的拉力測試試件是使用前的狀態(tài)未經(jīng)改變的完整的緊固件產(chǎn)品。
注2：A——Machined from annealed or solution-annealed stock thus retaining the properties of the original material, or hot-formed and solution-annealed.
AF——Headed and rolled from annealed stock and then reannealed.
AH——Solution annealed and age-hardened after forming.
CW——Headed and rolled from annealed stock thus acquining a degree of cold work; sizes 0.75 in. and larger may be hot worked and solution-annealed.
H——Hardened and tempered at 1050°F (565℃) minimum.
HT——Hardened and tempered at 525°F (274℃) minimum.
SH——Machined from strain hardened stock or cold-worked to develop the specified properties.
1 近似對照表 沉淀硬化型不銹鋼
中國 中國臺灣 日本 韓國 美國 國際標(biāo)準(zhǔn)組織 德國 法國 歐標(biāo)
GB ISC CNS JIS KS ASTM UNS ISO 數(shù)字牌號 DIN EN/DIN W-Nr. NF EN/NF EN 數(shù)字牌號
05Cr17Ni4Cu4Nb
(0Cr17Ni4Cu4Nb) 		S51740 630 SUS 630 STS 630 630 S17400 X5CrNiCuNb 16-4 4542-174-00-I X5CrNiCuNb 17-4 1.4542 Z6CNU 17-04 X5CrNiCuNb 16-4 1.4542
2 近似對照表 沉淀硬化型耐熱鋼
中國 中國臺灣 日本 韓國 美國 國際標(biāo)準(zhǔn)組織 德國 法國 歐標(biāo)
GB ISC CNS JIS KS ASTM UNS ISO DIN EN/DIN W-Nr. NF EN/NF EN 數(shù)字牌號
05Cr17Ni4Cu4Nb
(0Cr17Ni4Cu4Nb) 		S51740 630 SUS 630 STS 630 630 S17400 X5CrNiCuNb 16-4 X5CrNiCuNb 17-4 1.4542 Z6CNU 17-04 X5CrNiCuNb 16-4 1.4542