F593 316L簡(jiǎn)介

牌號(hào) F593 316L
美國(guó)UNS S31603
對(duì)應(yīng)標(biāo)準(zhǔn) ASTM F593-2017
不銹鋼螺栓、六角螺釘和螺柱標(biāo)準(zhǔn)規(guī)范
Standard specification for stainless steel bolts, hex cap screws, and studs
歸類(lèi) 奧氏體不銹鋼
F593 316L 化學(xué)元素成分含量(%)
成分 C Si Mn P S Cr Ni Mo
最小值 - - - - - 16 10 2
最大值 0.03 1 2 0.045 0.03 18 14 3
碳當(dāng)量計(jì)算
F593 316L 機(jī)械性能
公稱直徑
inch
試樣		 熱處理或狀態(tài)
抗拉強(qiáng)度
σb
ksi 		屈服點(diǎn)
σs
ksi 		斷后伸長(zhǎng)率或延伸率
δ
% 		硬度
HBW
1/4 ~ 1-1/2 (全尺寸) AF 65~85 ≥20 HR (B85 max)
1/4 ~ 1-1/2 (全尺寸) A 75~100 ≥30 HR (B65~95)
1/4 ~ 5/8 (全尺寸) CW1 100~150 ≥65 HR (B95~C32)
3/4 ~ 1-1/2 (全尺寸) CW2 85~140 ≥45 HR (B80~C32)
1/4 ~ 5/8 (全尺寸) SH1 120~160 ≥95 HR (C24~C36)
3/4 ~ 1 (全尺寸) SH2 110~150 ≥75 HR (C20~C32)
1-1/8 ~ 1-1/4 (全尺寸) SH3 100~140 ≥60 HR (B95~C30)
1-3/8 ~ 1-1/2 (全尺寸) SH4 95~130 ≥45 HR (B90~C28)
1/4 ~ 1-1/2 (機(jī)加工) AF ≥60 ≥20 ≥40
1/4 ~ 1-1/2 (機(jī)加工) A ≥70 ≥30 ≥30
1/4 ~ 5/8 (機(jī)加工) CW1 ≥95 ≥60 ≥20
3/4 ~ 1-1/2 (機(jī)加工) CW2 ≥80 ≥40 ≥25
1/4 ~ 5/8 (機(jī)加工) SH1 ≥115 ≥90 ≥12
3/4 ~ 1 (機(jī)加工) SH2 ≥105 ≥70 ≥15
1-1/8 ~ 1-1/4 (機(jī)加工) SH3 ≥95 ≥55 ≥20
1-3/8 ~ 1-1/2 (機(jī)加工) SH4 ≥90 ≥40 ≥28
注1： “全尺寸”指的拉力測(cè)試試件是使用前的狀態(tài)未經(jīng)改變的完整的緊固件產(chǎn)品。
注2：A——Machined from annealed or solution-annealed stock thus retaining the properties of the original material, or hot-formed and solution-annealed.
AF——Headed and rolled from annealed stock and then reannealed.
AH——Solution annealed and age-hardened after forming.
CW——Headed and rolled from annealed stock thus acquining a degree of cold work; sizes 0.75 in. and larger may be hot worked and solution-annealed.
H——Hardened and tempered at 1050°F (565℃) minimum.
HT——Hardened and tempered at 525°F (274℃) minimum.
SH——Machined from strain hardened stock or cold-worked to develop the specified properties.
近似對(duì)照表 奧氏體不銹鋼
中國(guó) 中國(guó)臺(tái)灣 日本 韓國(guó) 美國(guó) 國(guó)際標(biāo)準(zhǔn)組織 德國(guó) 法國(guó) 歐標(biāo) 俄羅斯 瑞典 英國(guó)
GB ISC CNS JIS KS ASTM UNS ISO 數(shù)字牌號(hào) DIN EN/DIN W-Nr. NF EN/NF EN 數(shù)字牌號(hào) GOST SS BS EN/BS
022Cr17Ni12Mo2
(00Cr17Ni14Mo2) 		S31603 316L SUS 316L STS 316L 316L S31603 X2CrNiMo 17-12-2
X2CrNiMo17-12-3 		4404-316-03-I
4432-316-03-I 		X2CrNiMo 18-14-3
(X2CrNiMo 18-12) 		1.4435 Z2CND 17-13 X2CrNiMo 17-12-2
X2CrNiMo17-12-3 		1.4404
1.4432 		03Х17Н14М2 2353 316S11
316S12