316C12LT196簡介

牌號 316C12LT196
對應(yīng)標(biāo)準(zhǔn) BS 3100-1991
一般工程用鑄鋼件
Specification for Steel castings for general engineering purposes
歸類 鑄鋼
性能 耐腐蝕
標(biāo)簽 奧氏體不銹鑄鋼
316C12LT196 化學(xué)元素成分含量(%)
成分 C Si Mn P S Cr Ni Mo
最小值 - - - - - 17 9 2
最大值 0.03 1.5 2 0.04 0.04 21 - 3
碳當(dāng)量計(jì)算
316C12LT196 機(jī)械性能
熱處理或狀態(tài)
抗拉強(qiáng)度
σb
Mpa 		屈服點(diǎn)
σs
Mpa 		斷后伸長率或延伸率
δ
% 		沖擊吸收能量
KV2
J
ST(1050°C~1150°C) ≥430 1% proof stress Rp1.0 min
≥215		 ≥26 -196°C
≥41
A=for anneal by heating to a temperature above the AC3 and cool in the furnace
N=for normalize by heating to a temperature above the AC3 and cool in still air
OQ=for quench into oil from a temperature above the AC3
WQ=for quench into water from a temperature above the AC3
AH=for air harden by heating to a temperature above the AC3 and cool in air at a rate fast enough to produce a hardened microstructure
T=for temper by heating to a temperature below AC1
ST=for solution treat by heating to temperature high enough to dissolve and any intermetallic phases followed by a rapid cool.