347C17簡介

牌號 347C17
對應(yīng)標(biāo)準(zhǔn) BS 3100-1991
一般工程用鑄鋼件
Specification for Steel castings for general engineering purposes
歸類 鑄鋼
性能 耐腐蝕
標(biāo)簽 奧氏體不銹鑄鋼 有磁性
347C17 化學(xué)元素成分含量(%)
成分 C Si Mn P S Cr Ni 更多
最小值 - - - - - 18 9 Nb:8C~1
最大值 0.08 1.5 2 0.04 0.04 21 12
碳當(dāng)量計算
347C17 機械性能
熱處理或狀態(tài)
抗拉強度
σb
Mpa 		屈服點
σs
Mpa 		斷后伸長率或延伸率
δ
%
ST(1000°C~1100°C) ≥480 1% proof stress Rp1.0 min
≥215		 ≥22
A=for anneal by heating to a temperature above the AC3 and cool in the furnace
N=for normalize by heating to a temperature above the AC3 and cool in still air
OQ=for quench into oil from a temperature above the AC3
WQ=for quench into water from a temperature above the AC3
AH=for air harden by heating to a temperature above the AC3 and cool in air at a rate fast enough to produce a hardened microstructure
T=for temper by heating to a temperature below AC1
ST=for solution treat by heating to temperature high enough to dissolve and any intermetallic phases followed by a rapid cool.
1 近似對照表 耐蝕鑄鋼（不銹鋼鑄件）
中國 日本 美國 德國 法國 英國
GB JIS ASTM DIN EN/DIN W-Nr. NF EN/NF BS EN/BS
ZG0Cr18Ni9Ti SUS21 CF8C G-X7CrNiNb 18 9 1.4552 Z6CNNb18.10M 347C17
2 近似對照表 耐熱鑄鋼和耐熱合金鑄件
中國 日本 美國 德國 法國 俄羅斯 英國
GB JIS ASTM UNS DIN EN/DIN W-Nr. NF EN/NF GOST BS EN/BS
ZG0Cr18Ni9Ti SCS21 CF8C J92710 G-X5CrNiNb18 9 1.4552 Z4CNNb19.10M 08Х18Н9Т 347C17