全球鋼材百科網
317C16簡介

牌號 317C16
對應標準 BS 3100-1991
一般工程用鑄鋼件
Specification for Steel castings for general engineering purposes
歸類 鑄鋼
性能 耐腐蝕
標簽 奧氏體不銹鑄鋼 有磁性
317C16 化學元素成分含量(%)
成分 C Si Mn P S Cr Ni Mo
最小值 - - - - - 17 9 3
最大值 0.08 1.5 2 0.04 0.04 21 - 4
碳當量計算
317C16 機械性能
熱處理或狀態(tài)
抗拉強度
σb
Mpa 		屈服點
σs
Mpa 		斷后伸長率或延伸率
δ
%
ST(1050°C~1150°C) ≥480 1% proof stress Rp1.0 min
≥240		 ≥22
A=for anneal by heating to a temperature above the AC3 and cool in the furnace
N=for normalize by heating to a temperature above the AC3 and cool in still air
OQ=for quench into oil from a temperature above the AC3
WQ=for quench into water from a temperature above the AC3
AH=for air harden by heating to a temperature above the AC3 and cool in air at a rate fast enough to produce a hardened microstructure
T=for temper by heating to a temperature below AC1
ST=for solution treat by heating to temperature high enough to dissolve and any intermetallic phases followed by a rapid cool.
近似對照表 耐熱鑄鋼和耐熱合金鑄件
美國 德國 英國
ASTM UNS DIN EN/DIN W-Nr. BS EN/BS
CG-8M J9300 G-X6CrNiMo17 13 1.4448 317C16