309C35簡(jiǎn)介

牌號(hào) 309C35
對(duì)應(yīng)標(biāo)準(zhǔn) BS 3100-1991
一般工程用鑄鋼件
Specification for Steel castings for general engineering purposes
歸類(lèi) 鑄鋼
性能 耐腐蝕
標(biāo)簽 耐熱不銹鑄鋼
309C35 化學(xué)元素成分含量(%)
成分 C Si Mn P S Cr Ni Mo
最小值 0.2 - - - - 24 11 -
最大值 0.5 1.5 2 0.04 0.04 28 14 1.5
碳當(dāng)量計(jì)算
309C35 機(jī)械性能
熱處理或狀態(tài)
抗拉強(qiáng)度
σb
Mpa 		斷后伸長(zhǎng)率或延伸率
δ
%
As cast ≥510 ≥7
A=for anneal by heating to a temperature above the AC3 and cool in the furnace
N=for normalize by heating to a temperature above the AC3 and cool in still air
OQ=for quench into oil from a temperature above the AC3
WQ=for quench into water from a temperature above the AC3
AH=for air harden by heating to a temperature above the AC3 and cool in air at a rate fast enough to produce a hardened microstructure
T=for temper by heating to a temperature below AC1
ST=for solution treat by heating to temperature high enough to dissolve and any intermetallic phases followed by a rapid cool.