334C11簡(jiǎn)介

牌號(hào) 334C11
對(duì)應(yīng)標(biāo)準(zhǔn) BS 3100-1991
一般工程用鑄鋼件
Specification for Steel castings for general engineering purposes
歸類 鑄鋼
性能 耐腐蝕
標(biāo)簽 耐熱鎳合金鑄鋼
334C11 化學(xué)元素成分含量(%)
成分 C Si Mn P S Cr Ni Mo
最小值 - - - - - 10 55 -
最大值 0.75 3 2 0.05 0.05 20 65 1.5
334C11 機(jī)械性能
熱處理或狀態(tài)
抗拉強(qiáng)度
σb
屈服點(diǎn)
σs
斷后伸長(zhǎng)率或延伸率
δ
% 		硬度
HBW 		沖擊吸收能量
KV2
J
N或N+T或QQ+T或WQ+T 540~690 ≥320 ≥16 152~207 ≥30
A=for anneal by heating to a temperature above the AC3 and cool in the furnace
N=for normalize by heating to a temperature above the AC3 and cool in still air
OQ=for quench into oil from a temperature above the AC3
WQ=for quench into water from a temperature above the AC3
AH=for air harden by heating to a temperature above the AC3 and cool in air at a rate fast enough to produce a hardened microstructure
T=for temper by heating to a temperature below AC1
ST=for solution treat by heating to temperature high enough to dissolve and any intermetallic phases followed by a rapid cool.