全球鋼材百科網(wǎng)
420C29簡(jiǎn)介

牌號(hào) 420C29
對(duì)應(yīng)標(biāo)準(zhǔn) BS 3100-1991
一般工程用鑄鋼件
Specification for Steel castings for general engineering purposes
歸類 鑄鋼
性能 耐腐蝕
標(biāo)簽 不銹鋼鑄鋼
420C29 化學(xué)元素成分含量(%)
成分 C Si Mn P S Cr Ni Cu ①
最小值 - - - - - 11.5 - -
最大值 0.2 1 1 0.04 0.04 13.5 1 0.3
①殘余元素 碳當(dāng)量計(jì)算
420C29 機(jī)械性能
熱處理或狀態(tài)
抗拉強(qiáng)度
σb
Mpa 		屈服點(diǎn)
σs
Mpa 		斷后伸長(zhǎng)率或延伸率
δ
%
AH+T或OQ+T(T at 750°C max) ≥690 ≥465 ≥11
A=for anneal by heating to a temperature above the AC3 and cool in the furnace
N=for normalize by heating to a temperature above the AC3 and cool in still air
OQ=for quench into oil from a temperature above the AC3
WQ=for quench into water from a temperature above the AC3
AH=for air harden by heating to a temperature above the AC3 and cool in air at a rate fast enough to produce a hardened microstructure
T=for temper by heating to a temperature below AC1
ST=for solution treat by heating to temperature high enough to dissolve and any intermetallic phases followed by a rapid cool.
1 近似對(duì)照表 耐蝕鑄鋼（不銹鋼鑄件）
中國(guó) 中國(guó)臺(tái)灣 日本 韓國(guó) 美國(guó) 德國(guó) 法國(guó) 俄羅斯 英國(guó)
GB ISC CNS JIS KS ASTM UNS DIN EN/DIN W-Nr. NF EN/NF GOST BS EN/BS
ZG20Cr13 C54200 SCS 2 SCS 2 SSC 2 CA40 J91153 GXCr20Ni14 1.4027 Z20C13M 20Х13Л 420C29
2 近似對(duì)照表 耐蝕鑄鋼（不銹鋼鑄件）
中國(guó) 日本 德國(guó) 法國(guó) 俄羅斯 英國(guó)
GB JIS DIN EN/DIN W-Nr. NF EN/NF GOST BS EN/BS
ZG2Cr13Ni SUS2 G-X20Cr14 1.4027 Z20C 13M 20Х13Л 420C29
3 近似對(duì)照表 耐熱鑄鋼和耐熱合金鑄件
中國(guó) 日本 美國(guó) 德國(guó) 法國(guó) 俄羅斯 英國(guó)
GB JIS ASTM UNS DIN EN/DIN W-Nr. NF EN/NF GOST BS EN/BS
ZG2Cr13 SCS2 CA40 J91153 G-X20Cr14 1.4027 Z20C13M 20Х13Л 420C29
全球鋼材百科網(wǎng)