330C11簡介

牌號 330C11
對應(yīng)標(biāo)準(zhǔn) BS 3100-1991
一般工程用鑄鋼件
Specification for Steel castings for general engineering purposes
歸類 鑄鋼
性能 耐腐蝕
標(biāo)簽 耐熱不銹鑄鋼
330C11 化學(xué)元素成分含量(%)
成分 C Si Mn P S Cr Ni Mo
最小值 0.35 - - - - 13 33 -
最大值 0.55 1.5 2 0.04 0.04 17 37 1.5
碳當(dāng)量計算
330C11 機械性能
熱處理或狀態(tài)
抗拉強度
σb
Mpa 		斷后伸長率或延伸率
δ
%
As cast ≥450 ≥3
A=for anneal by heating to a temperature above the AC3 and cool in the furnace
N=for normalize by heating to a temperature above the AC3 and cool in still air
OQ=for quench into oil from a temperature above the AC3
WQ=for quench into water from a temperature above the AC3
AH=for air harden by heating to a temperature above the AC3 and cool in air at a rate fast enough to produce a hardened microstructure
T=for temper by heating to a temperature below AC1
ST=for solution treat by heating to temperature high enough to dissolve and any intermetallic phases followed by a rapid cool.
近似對照表 耐熱鑄鋼和耐熱合金鑄件
中國 中國臺灣 日本 韓國 美國 國際標(biāo)準(zhǔn)組織 德國 法國 英國
GB ISC CNS JIS KS ASTM UNS ISO DIN EN/DIN W-Nr. NF EN/NF BS EN/BS
ZG40Ni35Cr17Si2 C53931 SCH 15 SCH 15X HRSC 15 HT J94605 GX40NiCrSi35-17 GX40NiCrSi35-17 1.4806 GX40NiCrSi35-17 330C11