302C25簡介

牌號 302C25
對應(yīng)標(biāo)準(zhǔn) BS 3100-1991
一般工程用鑄鋼件
Specification for Steel castings for general engineering purposes
歸類 鑄鋼
性能 耐腐蝕
標(biāo)簽 奧氏體不銹鑄鋼 有磁性
302C25 化學(xué)元素成分含量(%)
成分 C Si Mn P S Cr Ni
最小值 - - - - - 17 8
最大值 0.12 1.5 2 0.04 0.04 21 -
碳當(dāng)量計算
302C25 機械性能
熱處理或狀態(tài)
抗拉強度
σb
Mpa 		屈服點
σs
Mpa 		斷后伸長率或延伸率
δ
%
ST(1000°C~1100°C) ≥480 1% proof stress Rp1.0 min
≥240		 ≥26
A=for anneal by heating to a temperature above the AC3 and cool in the furnace
N=for normalize by heating to a temperature above the AC3 and cool in still air
OQ=for quench into oil from a temperature above the AC3
WQ=for quench into water from a temperature above the AC3
AH=for air harden by heating to a temperature above the AC3 and cool in air at a rate fast enough to produce a hardened microstructure
T=for temper by heating to a temperature below AC1
ST=for solution treat by heating to temperature high enough to dissolve and any intermetallic phases followed by a rapid cool.
1 近似對照表 耐蝕鑄鋼（不銹鋼鑄件）
中國 日本 美國 德國 法國 英國
GB JIS ASTM DIN EN/DIN W-Nr. NF EN/NF BS EN/BS
ZG1Cr18Ni9 SUS12 CF20 G-X10CrNi 18 8 1.4312 Z10CN18.9M 302C25
2 近似對照表 耐熱鑄鋼和耐熱合金鑄件
中國 日本 德國 法國 俄羅斯 英國
GB JIS DIN EN/DIN W-Nr. NF EN/NF GOST BS EN/BS
ZG1Cr18Ni9 SCS12
SCS13A 		G-X10CrNi18 8 1.4312 Z10CN18.9M 10Х18Н9Л 302C25