S235B簡介

牌號 S235B
對應標準 ISO 683-18-2014
熱處理鋼、合金鋼和易切削鋼 -- 第18部分：光面鋼制品
Bright steel products
歸類 合金鋼
S235B 化學元素成分含量(%)
成分 C Mn P S ① Cu ③ N ②
t≤40mm 最小值 - - - - - -
最大值 0.17 1.4 0.04 0.04 0.55 0.012
成分 C Mn P S ① Cu ③ N ②
40mm＜t≤100mm 最小值 - - - - - -
最大值 0.2 1.4 0.04 0.04 0.55 0.012
① For long products. the max. S content may be increased for improved machinablility ba 0,005 % by agreement if the steel is treated to modify the sulphide morphology and if the chemical composition shows min 0,0020 % Ca.
② The maximum value for nitrogen does not apply if the chemical composition shows a minimum total Al content of 0,020 % or, alternalively, minimum 0,015 % acid soluble Al or if s ufficient other N-binding elements are present. In this case, the N-binding elements shall be mentioned in the inspection document.
③ Cu contenl above 0,40 % can cause hot shortness during hot forming. 碳當量計算
S235B 機械性能
厚度
t
mm		 熱處理或狀態(tài)
抗拉強度
σb
Mpa 		屈服點
σs
Mpa 		斷后伸長率或延伸率
δ
% 		硬度
HBW
5≤t≤10 Cold drawn (+C) 470~840 ≥355 ≥8
10＜t≤16 Cold drawn (+C) 420~770 ≥300 ≥9
16＜t≤40 Cold drawn (+C) 390~730 ≥260 ≥10
40＜t≤63 Cold drawn (+C) 380~670 ≥235 ≥11
63＜t≤100 Cold drawn (+C) 360~640 ≥215 ≥11
16＜t≤100 As-rolled + peeled (+SH) 360~510 107~152
近似對照表 碳素結構鋼和工程用鋼
中國 國際標準組織 歐標
GB ISO EN 數(shù)字牌號
Q235B S235B S235JRC 1.0122