S420J2W簡(jiǎn)介

牌號(hào) S420J2W
歐標(biāo)鋼號(hào) 1.8949
對(duì)應(yīng)標(biāo)準(zhǔn) EN 10025-5-2019
熱軋結(jié)構(gòu)鋼-第5部分：耐候結(jié)構(gòu)鋼
Hot rolled products of structural steels-Part 5: Technical delivery conditions for structural steels with improved atmospheric corrosion resistance
歸類(lèi) 合金鋼
標(biāo)簽 耐候結(jié)構(gòu)鋼
S420J2W 化學(xué)元素成分含量(%)
成分 C Si Mn P S Cr Ni ③ Cu Mo ③ N Zr ③
長(zhǎng)形產(chǎn)品 最小值 - - 0.5 - - 0.4 - 0.25 - - -
最大值 0.2 0.65 1.35 0.03 0.03 0.8 0.65 0.55 0.35 0.025 0.15
成分 C Si Mn P S Cr Ni ③ Cu Mo ③ N Zr ③
最小值 - - 0.5 - - 0.4 - 0.25 - - -
最大值 0.2 0.65 1.35 0.035 0.035 0.8 0.65 0.55 0.35 0.025 0.15
①FN=rimming steels not permitted(不允許沸騰鋼)；FF=fully killed steel(完全鎮(zhèn)靜鋼)
②The steels contain at least one of the following elements: Al total≥0.02%，Nb:0.015~0.06%，V:0.02~0.12%，Ti:0.02~0.1%。If these elements are used in combination, at least one them shall be present with the minimum content indicated。(鋼應(yīng)至少含有下列元素之一:Al總含量為≥0.020%，Nb:0.015 ~ 0.060%，V:0.02 ~ 0.12%，Ti:0.02 ~ 0.10%。如果將這些元素組合使用，其中至少有一種元素應(yīng)具有所示的最低含量。)
③鋼中Ni、Mo、Zr含量可達(dá)的最大值
④當(dāng)Si的最低含量為0.15%時(shí)，Cr含量可降至0.37% 碳當(dāng)量計(jì)算
S420J2W 機(jī)械性能
厚度
t
mm		 抗拉強(qiáng)度
σb
Mpa 		屈服點(diǎn)
σs
Mpa 		斷后伸長(zhǎng)率或延伸率
δ
%
t＜3 520~680 ≥420 ≥15
3≤t≤16 500~660 ≥420 ≥19
16＜t≤40 500~660 ≥400 ≥19
40＜t≤63 500~660 ≥390 ≥18
63＜t≤80 500~660 ≥380 ≥17
80＜t≤100 500~660 ≥370 ≥17
100＜t≤150 460~620 ≥365 ≥16