全球鋼材百科網(wǎng)
S355D簡(jiǎn)介

牌號(hào) S355D
對(duì)應(yīng)標(biāo)準(zhǔn) ISO 683-18-2014
熱處理鋼、合金鋼和易切削鋼 -- 第18部分：光面鋼制品
Bright steel products
歸類 合金鋼
S355D 化學(xué)元素成分含量(%)
成分 C Si Mn P S ① Cu ②
t≤40mm 最小值 - - - - - -
最大值 0.2 0.55 1.6 0.03 0.03 0.55
成分 C Si Mn P S ① Cu ②
40mm＜t≤100mm 最小值 - - - - - -
最大值 0.22 0.55 1.6 0.03 0.03 0.55
① For long products. the max. S content may be increased for improved machinablility ba 0,005 % by agreement if the steel is treated to modify the sulphide morphology and if the chemical composition shows min 0,0020 % Ca.
② Cu contenl above 0,40 % can cause hot shortness during hot forming. 碳當(dāng)量計(jì)算
S355D 機(jī)械性能
厚度
t
mm		 熱處理或狀態(tài)
抗拉強(qiáng)度
σb
Mpa 		屈服點(diǎn)
σs
Mpa 		斷后伸長(zhǎng)率或延伸率
δ
% 		硬度
HBW
5≤t≤10 Cold drawn (+C) 630~950 ≥520 ≥6
10＜t≤16 Cold drawn (+C) 580~880 ≥450 ≥7
16＜t≤40 Cold drawn (+C) 530~850 ≥350 ≥8
40＜t≤63 Cold drawn (+C) 500~770 ≥335 ≥9
63＜t≤100 Cold drawn (+C) 470~740 ≥315 ≥9
16＜t≤100 As-rolled + peeled (+SH) 470~630 140~187
近似對(duì)照表 碳素結(jié)構(gòu)鋼和工程用鋼
中國(guó) 國(guó)際標(biāo)準(zhǔn)組織 德國(guó) 歐標(biāo) 英國(guó)
GB ISO DIN EN/DIN EN 數(shù)字牌號(hào) BS EN/BS
Q345D S355D St52-3N S355J2C 1.0579 50D8